Modeling oxidation damage of continuous fiber reinforced ceramic matrix composites
ceramic matrix composites、fiber reinforced、oxidation、high temperature、micromechanical model、mechanical properties、pyrolytic carbon、growth mechanism、tensile modulus、fiber strength、Carbon fiber、application、SiC fiber、direction、presents、CMCs、theory、During、C/SiC、based