INTERFACIAL MASS TRANSPORT IN OXIDE CRYSTAL GROWTH
@@ A space high temperature in situobservation instrument (SHITISOI) is dedicated to visualize and record the whole growth process of oxide crystal in high temperature melts and solutions. Model experiments using transparent liquids such as KNbO3,Li2B4O7+KNbO3 were chosen to investigate effects of interracial mass transport in oxide crystal growth. For the scaling of the coupled velocity, heat and concentration fields in KNbO3 crystal growth, a rotating crystal growth process was performed and the widths of interfacial concentration, heat and momentum transition zones (The ”boundary layers”) are obtained, which are 7.5×10-a, 8.6×10-2 and 4.4×10-1 cm,respectively. Hence one can expect that interfacial concentration gradient will be confined to a narrow layer and in region of major concentration change at the in terface. In order to study a mechanism based on the interfacial mass transport resulting from hydrodynamics, the growth of KNbO3 grain in high temperature Li2B4O7 and KNbO3 solutin was studied. The result shows that the pivotal feature in the KNbO3 crystal growth is the initiated by KNbO3 solute surface tension gra dient which is caused by the slow diffusion of KNbO3 solutes. Direct comparison of the model predictions and experimental observed phenomena demonstrate the predictive capability of this model.
CRYSTAL GROWTH、crystal growth、interfacial concentration、high temperature、mass transport、concentration gradient、concentration fields、surface tension
22
O6(化学)
2004-01-08（万方平台首次上网日期，不代表论文的发表时间）
共1页
160-160