Characteristics of Welding Crack Defects and Failure Mode in Resistance Spot Welding of DP780 Steel
Resistance Spot Welding、welded joints、surface crack、failure mode、resistance spot welding、transgranular fracture、intergranular fracture、mechanical properties、electron microscopy、tensile test、strength of、inner crack、mode of